Aluminum powder, general classification
Range of application of aluminum powders (printing inks, paints, coatings, plastics and other industrial applications).
Inks – flexographic/gravure printing
Paints, coatings, varnishes, aerosols
Inks – offset printing
Industrial paints based on solvent, various coatings
Plastics
Decorative and/or protective coating on roll materials (metal, etc.)
Screen printing on textiles and other support
Grade |
Particle distribution upon size |
Apparent density |
Optical characteristics |
Recommended application |
|
D10* |
D50** |
D90*** |
(g/cm3) |
|
|
|
|
|
|
|
02 |
28 |
86 |
180 |
0.28 |
coarse/very bright |
|
|
|
|
|
|
04 |
23 |
76 |
165 |
0.28 |
coarse/very bright |
|
|
|
|
|
|
06 |
16 |
58 |
135 |
0.28 |
coarse/very bright |
|
|
|
|
|
|
08 |
13 |
45 |
110 |
0.25 |
coarse/very bright |
|
|
|
|
|
|
880 |
9 |
32 |
78 |
0.25 |
мелкий/яркий |
|
|
|
|
|
|
8880 |
6 |
21 |
55 |
0.23 |
fine/bright |
|
|
|
|
|
|
8980 |
4 |
14 |
42 |
0.23 |
fine/bright |
|
|
|
|
|
|
024 |
2.5 |
9.5 |
28 |
0.23 |
very fine/large range |
|
|
|
|
|
|
76000 |
2.5 |
8.5 |
25 |
0.18 |
very fine/large range |
|
|
|
|
|
|
030 |
2.5 |
8 |
23 |
0.22 |
very fine/large range |
|
|
|
|
|
|
032 |
2 |
7 |
20 |
0.20 |
very fine/large range |
|
|
|
|
|
|
80000/A |
2 |
7 |
20 |
0.23 |
very fine/large range |
|
|
|
|
|
|
The data given in the table are for reference only.
Aluminum powders contain more than 99.7% aluminum.
All grades of aluminum powders in this section are intended for producing of solvent-based compositions.
A dispersion system of formulations with the aforementioned aluminum powder grades is achieved by premixing with a small amount of a solvent and slowly rotating in a mixer, followed by the addition of a binder/varnish and other components.
D10*– 10% of the particles are finer than this value.
D50** – 50% of the particles are finer than this value.
D90***– 90% of the particles are finer than this value.
Products with modified characteristics can also be made to order.
Aluminum powder for cellular concrete
Grade |
Particle distribution upon size |
Apparent density |
Optical characteristics |
|
D10* |
D50** |
D90*** |
g/cm³ |
|
ATF9 (OTF9) |
6 |
23 |
55 |
0.15 |
very fine |
ATF6 (OTF6) |
8 |
27 |
70 |
0.15 |
very fine |
YTF/2 |
8 |
27 |
64 |
0.15 |
very fine |
YM/2 |
8 |
27 |
64 |
0.15 |
very fine |
ATF5 (OTF5) |
8 |
30 |
72 |
0.15 |
fine |
ATF4 (OTF4) |
10 |
34 |
78 |
0.14 |
fine |
ATF1 (OTF1) |
18 |
68 |
170 |
0.14 |
coarse |
AT9 (OT9) |
6 |
23 |
55 |
0.16 |
very fine |
AT6 (OT6) |
8 |
27 |
69 |
0.15 |
very fine |
AM6 |
8 |
27 |
69 |
0.15 |
very fine |
YT/2 |
8 |
28 |
72 |
0.15 |
very fine |
BTF9 |
6 |
23 |
62 |
0.17 |
very fine |
BTF6 |
7 |
27 |
68 |
0.16 |
very fine |
BYT/2 |
7 |
26 |
62 |
0.16 |
very fine |
BTF5 |
8 |
32 |
85 |
0.15 |
fine |
BTF4 |
10 |
34 |
78 |
0.16 |
fine |
BTF1 |
17 |
65 |
150 |
0.18 |
coarse |
AG/6 |
7 |
25 |
60 |
0.2 |
very fine |
AG/5 |
9 |
30 |
68 |
0.2 |
fine |
AG/4 |
10 |
34 |
74 |
0.2 |
fine |
BG6 |
7 |
25 |
60 |
0.17 |
very fine |
BG5 |
9 |
30 |
68 |
0.17 |
fine |
BG4 |
10 |
34 |
74 |
0.17 |
fine |
D10*– 10% of the particles are finer than this value.
D50** – 50% of the particles are finer than this value.
D90***– 90% of the particles are finer than this value.
Aluminum Pastes for Plastics
Grade
|
Particle distribution upon size
|
Apparent density
|
Optical characteristics
|
|
D10 (µm)
|
D50(µm)
|
D90 (µm)
|
(g/cm³)
|
|
02/ME/80-20
|
|
28
|
86
|
180
|
0.28
|
coarse/very bright
|
04/ME/80-20
|
|
23
|
76
|
165
|
0.28
|
coarse/very bright
|
06/ME/80-20
|
|
16
|
58
|
135
|
0.28
|
coarse/very bright
|
08/ME/80-20
|
|
13
|
45
|
110
|
0.25
|
coarse/very bright
|
880/ME/80-20
|
|
9
|
32
|
78
|
0.25
|
fine/bright
|
8880/ME/80-20
|
|
6
|
21
|
55
|
0.23
|
fine/bright
|
8980/ME/80-20
|
|
4
|
14
|
42
|
0.23
|
fine/bright
|
024/ME/80-20
|
|
2.5
|
9.5
|
28
|
0.23
|
very fine/large range
|
76000/ME/80-20
|
|
2.5
|
8.5
|
25
|
0.18
|
very fine/large range
|
030/ME/80-20
|
|
2.5
|
8
|
23
|
0.22
|
very fine/large range
|
032/ME/80-20
|
|
2
|
7
|
20
|
0.23
|
very fine/large range
|
80000A/ME/80-20
|
|
2
|
7
|
19
|
0.23
|
very fine/large range
|
Aluminum paste for solvent-based inks
Grade
|
Particle distribution upon size
|
Optical characteristics
|
|
D10 (µm)
|
D50 (µm)
|
D90 (µm)
|
|
8980 / EA / 70-30
|
|
4
|
14
|
42
|
fine/bright
|
8980 / МПА / 70-30
|
|
4
|
14
|
42
|
fine/bright
|
80000A / EA / 70-30
|
|
2
|
7
|
19
|
very fine/large range
|
80000A / МПА / 70-30
|
|
2
|
7
|
19
|
very fine/large range
|
Aluminum paste for water-based inks
Grade
|
Particle distribution upon size
|
Optical characteristics
|
|
D10 (µm)
|
D50 (µm)
|
D90 (µm)
|
|
Aquastab 80000 / А / PM9B / 65-35
|
2
|
7
|
20
|
very fine/large range
|
Aquastab 8980 / PM9B / 65-35
|
4
|
15
|
42
|
fine/bright
|
Aluminum paste for screen printing on textiles and other support
Grade
|
Particle distribution upon size
|
Optical characteristics
|
|
D10 (µm)
|
D50 (µm)
|
D90 (µm)
|
|
О6 / DI / 70-30
|
|
16
|
58
|
130
|
coarse/very bright
|
О8 / DI / 70-30
|
|
13
|
45
|
105
|
coarse/very bright
|
8880 / DI / 70-30
|
|
6
|
21
|
55
|
fine/bright
|
80000 / А / DI / 70-30
|
|
2
|
7
|
19
|
very small/large range
|
90000 / А / DI / 70-30
|
|
2
|
5.5
|
16
|
very small/large range
|
Aluminum paste for cellular concrete
Grade
|
Particle distribution upon size
|
Apparent density
(g/cm3)
|
Optical characteristics
|
|
D10 (µm)
|
D50 (µm)
|
D90 (µm)
|
|
|
ATF9 (OTF9) / DEG1 / 70-30
|
6
|
23
|
55
|
0.15
|
very fine
|
ATF6 (OTF6) / DEG1 / 70-30
|
8
|
27
|
70
|
0.15
|
very fine
|
YTF / 2 / DEG1 / 70-30
|
8
|
27
|
64
|
0.15
|
very fine
|
ATF5 (OTF5) / DEG1 / 70-30
|
8
|
30
|
72
|
0.15
|
fine
|
ATF4 (OTF4) / DEG1 / 70-30
|
10
|
34
|
78
|
0.14
|
fine
|
AT9 (OT9) / DEG1 / 70-30
|
6
|
23
|
55
|
0.16
|
very fine
|
AT6 (OT6) / DEG1 / 70-30
|
8
|
27
|
69
|
0.15
|
very fine
|
Yt2 / DEG1 / 70-30
|
8
|
28
|
72
|
0.15
|
very fine
|
BTF9 / DEG1 / 70-30
|
6
|
23
|
62
|
0.17
|
very fine
|
BTF6 / DEG1 / 70-30
|
7
|
27
|
68
|
0.16
|
very fine
|
BTF5 / DEG1 / 70-30
|
8
|
32
|
85
|
0.15
|
fine
|
BTF4 / DEG1 / 70-30
|
10
|
34
|
78
|
0.16
|
fine
|
BTF1 / DEG1 / 70-30
|
17
|
65
|
150
|
0.18
|
coarse
|
AG6 / DEG1 / 70-30
|
7
|
25
|
60
|
0.2
|
very fine
|
AG5 / DEG1 / 70-30
|
9
|
30
|
68
|
0.2
|
fine
|
AG4 / DEG1 / 70-30
|
10
|
34
|
74
|
0.2
|
fine
|
BG6 / DEG1 / 70-30
|
7
|
25
|
60
|
0.17
|
very fine
|
BG5 / DEG / 70-30
|
9
|
30
|
68
|
0.17
|
fine
|
BG4 / DEG1 / 70-30
|
10
|
34
|
74
|
0.17
|
fine
|
Aluminum pastes for titanium dioxide
Grade
|
Particle distribution upon size
D50 (µm)
|
A8 / МАС / 65-35
|
32
|
A8 / MWS / 80-20
|
18
|
A8 / WAS / 60-40
|
32
|
Aluminum Granules
Grade
|
Particle size
|
В 0-1
|
Granules between 0 and 1 mm
|
В 0-3
|
Granules from 0 up to 3 mm
|
В 1-3
|
Granules between 1 and 3 mm
|